马来酸酐接枝PP

马来酸酐接枝PP价格：16000.00元/吨 最小起订量：1 吨 供货总量：3000 吨 发货期限：自买家付款之日起1天内发货 有效期至：长期有效

                                                                        马来酸酐接枝PP

特性：本品为马来酸酐接枝的PP共混物，外观：白色或淡黄色颗粒，接枝率：0.6-1.0%，熔融指数(190℃，2.16kg)：40-80g/10min。

Property:The product is the mixture that MAH was grafted onto PP.  Appearance: white or light yellow particle; Grafting ratio: 0.6-1.0%; MFR(190℃，2.16kg):40-80g/10min.

用途：１．用作玻纤和矿物填充聚丙烯的界面改性剂：聚丙烯接枝马来酸酐赋予了聚烯烃极性和可粘接性，只要加入少量(5%)的马来酸酐接枝聚丙烯，就可以大幅度提高聚丙烯与玻纤、滑石粉、云母等无机填料的粘合力。

２．用作聚丙烯和含有极性基团树脂合金的相容剂：马来酸酐接枝聚丙烯应用面广，可作为PA/PP，PA/PE共混合金的相容剂。

３．赋予聚丙烯涂覆性和喷漆性：添加(10%-20%)的接枝母粒，还可以改善聚丙烯的涂覆性和喷漆性能。

Usage: 1.Used as interface modifier in PP with filling glass-fiber and mineral: PP can be given polarity and adhesiveness if MAH was grafted onto it. Adding a small amount of HF-1 can improve widely tensile strength, tension strength, impact strength and adhesiveness in PP and glass-fiber, talc powder, mica, etc.

2.Used as compatibilizer in alloy of PP and resin which has polar group: HF-1 (grafted compound) was applied widely. It can be used as compatibilizer in blending alloy of PA/PP, PA/PE.

3.Given coating and sprayability: Adding the grafted master batch (10-20%) can develop coating and sprayability of PP.

表一（Figure 1）：PP树脂玻纤增强典型数据:（Typical data of PP/GF）

性能（Performance）	单位（Unit）	PP+GF30%	PP+ GF30%+5%(HF－1)
拉伸强度（Tensile strength）	MPa	43	88
弯曲强度（Flexural strength）	MPa	69	125
悬臂梁冲击强度 （Izod notched impact strength）	KJ/m2	6	14.5

表二（Figure 2）：PP树脂矿物填充典型数据（Typical data of mineral filling PP） 

性能（Performance）	单位(Unit)	PP+滑石 (talc power )20%	PP+滑石 (talc power )20%+5%(HF－1)
拉伸强度（Tensile strength）	MPa	35	47
弯曲强度（Flexural strength）	MPa	68	73
悬臂梁冲击强度 （Izod notched impact strength）	KJ/m2	5	8

使用方法：按比例与PP、PA等树脂混合造粒。、

Dosage: HF-1 and PA、PP and so on are in proportion to blending and making batch.

包装及储运：20Kg牛皮纸袋内衬塑料袋装，按非危险品，在干燥条件下储运，避日光、雨淋。

Packing, storage and transportation:Packed in 20Kg cow parchment takes with plastic takes inside. Not dang