PA6T价格：0.00元/ 供货总量：10 有效期至：长期有效
| PA6TCH230N三井化学株式会社技术指数 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 23℃,24小时在水里(2mmt,100℃) | ASTM D-570 | 0.3(3.0) | % |
| 物理性能 | 模具收缩率 | 2mmt | ASTM D-955 | 0.4(0.8) | % |
| 比重 | --- | ASTM D-792 | 1.63 | --- | |
| 机械性能 | 拉伸强度 | dry(moist) | ASTM D-638 | 160(140) | MPa |
| 拉伸伸长率 | dry(moist) | ASTM D-638 | 4(3) | % | |
| 弯曲强度 | dry(moist) | ASTM D-790 | 240(200) | MPa | |
| 弯曲模量 | dry(moist) | ASTM D-790 | 11000(8000) | MPa | |
| IZOD缺口冲击强度 | dry(moist) | ASTM D-256 | 80(90) | J/M | |
| 洛氏硬度 | --- | ASTM D-785 | 95 | M scale | |
| 电气性能 | 体积电阻率 | dry | ASTM D-257 | 1015 | Ω.cm |
| 介电常数 | 1016Hz,dry | ASTM D-150 | 4.0 | --- | |
| 损耗因数 | 1016Hz,dry | ASTM D-150 | 25 | --- | |
| Dielectric breakdown voltage | dry | ASTM D-149 | 25 | KV/mm | |
| 热 性 能 | 熔点 | --- | --- | 310 | ℃ |
| 玻璃转变温度 | --- | --- | 85 | ℃ | |
| 负荷挠曲温度 | --- | ASTM D-648 | 290 | ℃ | |
| 线性热膨胀系数 | --- | ASTM D-696 | 3.0(6.0) | ×10-5/℃ | |
| 阻燃性 | --- | UL 94 | V-0 | --- | |
| 其它性能 | Glass fiber content | --- | --- | 30 | % |
| 牌号 | CH230NN | 厂家(产地) | 日本东丽 |
| 用途级别 | 玻璃纤维增强 |